عنوان انگلیسی: Towards long lasting zirconia-based composites for dental implants: Transformation induced plasticity and its consequence on ceramic reliability
سال نشر: ۲۰۱۷
نویسنده: Helen Reveron,Marta Fornabaio,Paola Palmero,Tobias Fürderer,Erik Adolfsson,Vanni Lughi,Alois Bonifacio,Valter Sergo,Laura Montanaro,Jérôme Chevalier
تعداد صفحه فارسی: ۱۹ – تعداد صفحه انگلیسی: ۱۰
دانشگاه: Université de Lyon-INSA de Lyon, MATEIS CNRS UMR 5510, 20 Avenue Albert Einstein, F-69621 Villeurbanne Cedex, France b Department of Applied Science and Technology, INSTM R.U. PoliTO, LINCE Lab., Politecnico di Torino, Corso Duca degli Abruzzi, 24, 10129 Torino, Italy c DOCERAM, MOESCHTER GROUP Holding GmbH & Co. KG, Hesslingsweg 65 – ۶۷, ۴۴۳۰۹ Dortmund, Germany d Ceramic Materials, Swerea IVF AB, 431 53 Mölndal, Sweden e Dept. of Engineering and Architecture, University of Trieste, Via Valerio
نشریه: Process Safety and Environmental Protection
کیفیت ترجمه: ترجمه پلاس
چکیده
کامپوزیت های پایه زیرکونیا از طریق یک مسیر فرآوری نوآورانه توسعه یافتند که قادر به تنظیم ویژگی‌های ترکیبی و ریزساختاری بسیار دقیق هستند. سرامیک‌های زیرکونیا کاملا چگال با روکش پایدار (۸۴ درصد حجمی Ce-TZP) حاوی آلومینای هم محور (۸ درصد حجمی Al2O3 ) و هگزا آلومینات استرانسیم سوزنی (۸ درصد حجمی SrAl12O19) فازهای دوم با استفاده از تف جوشی متداول به دست آمد. این کار به بررسی تاثیر درجه پایدار زیرکونیا ( CeO2 در دامنه ۱۰ – ۱۱.۵ درصد مولی) بر خواص مکانیکی و قابلیت تغییر شکل مواد Ce – TZP – Al2O3 – SrAl12O19 می‌پردازد.
Abstract
Zirconia-based composites were developed through an innovative processing route able to tune compositional and microstructural features very precisely. Fully-dense ceria-stabilized zirconia ceramics (84 vol% Ce-TZP) containing equiaxed alumina (8 vol%Al 2 O 3 ) and elongated strontium hexa-aluminate (8 vol% SrAl 12 O 19 ) second phases were obtained by conventional sintering. This work deals with the effect of the zirconia stabilization degree (CeO 2 in the range 10.0–۱۱.۵ mol%) on the transformability and mechanical properties of Ce-TZP-Al 2 O 3 -SrAl 12 O 19 materials. Vickers hardness, biaxial flexural strength and Single-edge V-notched beam tests revealed a strong influence of ceria content on the mechanical properties. Composites with 11.0 mol% CeO 2 or above exhibited the classical behaviour of brittle ceramics, with no apparent plasticity and very low strain to failure. On the contrary, composites with 10.5 mol% CeO 2 or less showed large transformation-induced